Viable adhered Staphylococcus aureus highly reduced on novel antimicrobial sutures using chlorhexidine and octenidine to avoid surgical site infection (SSI)

Background Surgical sutures can promote migration of bacteria and thus start infections. Antiseptic coating of sutures may inhibit proliferation of adhered bacteria and avoid such complications. Objectives This study investigated the inhibition of viable adhering bacteria on novel antimicrobially coated surgical sutures using chlorhexidine or octenidine, a critical factor for proliferation at the onset of local infections. The medical need, a rapid eradication of bacteria in wounds, can be fulfilled by a high antimicrobial efficacy during the first days after wound closure. Methods As a pretesting on antibacterial efficacy against relevant bacterial pathogens a zone of inhibition assay was conducted with middle ranged concentrated suture coatings (22 μg/cm). For further investigation of adhering bacteria in detail the most clinically relevant Staphylococcus aureus (ATCC^®49230™) was used. Absorbable braided sutures were coated with chlorhexidine-laurate, chlorhexidine-palmitate, octenidine-laurate, and octenidine-palmitate. Each coating type resulted in 11, 22, or 33 μg/cm drug content on sutures. Scanning electron microscopy (SEM) was performed once to inspect the coating quality and twice to investigate if bacteria have colonized on sutures. Adhesion experiments were assessed by exposing coated sutures to S. aureus suspensions for 3 h at 37C. Subsequently, sutures were sonicated and the number of viable bacteria released from the suture surface was determined. Furthermore, the number of viable planktonic bacteria was measured in suspensions containing antimicrobial sutures. Commercially available sutures without drugs (Vicryl^®, PGA Resorba^®, and Gunze PGA), as well as triclosan-containing Vicryl^® Plus were used as control groups. Results Zone of inhibition assay documented a multispecies efficacy of novel coated sutures against tested bacterial strains, comparable to most relevant S. aureus over 48 hours. SEM pictures demonstrated uniform layers on coated sutures with higher roughness for palmitate coatings and sustaining integrity of coated sutures. Adherent S. aureus were found via SEM on all types of investigated sutures. The novel antimicrobial sutures showed significantly less viable adhered S. aureus bacteria (up to 6.1 log) compared to Vicryl^® Plus (0.5 log). Within 11 μg/cm drug-containing sutures, octenidine-palmitate (OL11) showed the highest number of viable adhered S. aureus (0.5 log), similar to Vicryl^® Plus. Chlorhexidine-laurate (CL11) showed the lowest number of S. aureus on sutures (1.7 log), a 1.2 log greater reduction. In addition, planktonic S. aureus in suspensions were highly inhibited by CL11 (0.9 log) represents a 0.6 log greater reduction compared to Vicryl^® Plus (0.3 log). Conclusions Novel antimicrobial sutures can potentially limit surgical site infections caused by multiple pathogenic bacterial species. Therefore, a potential inhibition of multispecies biofilm formation is assumed. In detail tested with S. aureus, the chlorhexidine-laurate coating (CL11) best meets the medical requirements for a fast bacterial eradication. This suture coating shows the lowest survival rate of adhering as well as planktonic bacteria, a high drug release during the first–clinically most relevant– 48 hours, as well as biocompatibility. Thus, CL11 coatings should be recommended for prophylactic antimicrobial sutures as an optimal surgical supplement to reduce wound infections. However, animal and clinical investigations are important to prove safety and efficacy for future applications.