Tungsten divertor erosion in all metal devices: Lessons from the ITER like wall of JET

G. J. Van Rooij, J. W. Coenen, L. Aho-Mantila, S. Brezinsek, M. Clever, R. Dux, M. Groth, K. Krieger, S. Marsen, G. F. Matthews, A. Meigs, R. Neu, S. Potzel, T. Pütterich, J. Rapp, M. F. Stamp

Research output: Contribution to journalArticlepeer-review

131 Scopus citations

Abstract

Tungsten erosion in the outer divertor of the JET ITER like wall was quantified by spectroscopy. Effective sputtering yields of typically 10 4 were measured in L-mode at ∼30 eV attached divertor conditions and beryllium was identified as the main cause of sputtering. The signature of prompt redeposition was observed in the analysis of WI 400.9 nm and WII 364 nm line ratios and indicative of >50% redeposition fractions. Inter- and intra-ELM sputtering were compared for an example of 10 Hz ELMs with 13 MW NBI heating, in which intra-ELM sputtering was found to dominate by a factor of 5. Nitrogen seeding initially increased the tungsten sputtering threefold due to higher extrinsic impurity levels and effectively reduced the tungsten sputtering when the divertor plasma temperature was decreased from the initial 25 eV down to 15 eV.

Original languageEnglish
Pages (from-to)S42-S47
JournalJournal of Nuclear Materials
Volume438
Issue numberSUPPL
DOIs
StatePublished - 2013
Externally publishedYes

Fingerprint

Dive into the research topics of 'Tungsten divertor erosion in all metal devices: Lessons from the ITER like wall of JET'. Together they form a unique fingerprint.

Cite this