Surface Oxygen Depletion of Layered Transition Metal Oxides in Li-Ion Batteries Studied by Operando Ambient Pressure X-ray Photoelectron Spectroscopy

A new operando spectro-electrochemical setup was developed to study oxygen depletion from the surface of layered transition metal oxide particles at high degrees of delithiation. An NCM111 working electrode was paired with a chemically delithiated LiFePO₄ counter electrode in a fuel cell-inspired membrane electrode assembly (MEA). A propylene carbonate-soaked Li-ion conducting ionomer served as an electrolyte, providing both good electrochemical performance and direct probing of the NCM111 particles during cycling by ambient pressure X-ray photoelectron spectroscopy. The irreversible emergence of an oxygen-depleted phase in the O 1s spectra of the layered oxide particles was observed upon the first delithiation to high state-of-charge, which is in excellent agreement with oxygen release analysis via mass spectrometry analysis of such MEAs. By comparing the metal oxide-based O 1s spectral features to the Ni 2p_3/2 intensity, we can calculate the transition metal-to-oxygen ratio of the metal oxide close to the particle surface, which shows good agreement with the formation of a spinel-like stoichiometry as an oxygen-depleted phase. This new setup enables a deeper understanding of interfacial changes of layered oxide-based cathode active materials for Li-ion batteries upon cycling.