Supported particle track etched polyimide membranes: A grazing incidence small-angle x-ray scattering study

Particle track etched polyimide membranes on silicon substrates covered with a native oxide layer are investigated. Preparation steps similar to the common classical particle track etched membrane production, giving rise to free-standing membranes, are successfully applied to the supported membranes. Polyimide films are used as a starting material for a template preparation based on high energy ion irradiation. The film/membrane structure is probed at different length scales by grazing incidence small-angle X-ray scattering at each individual preparation step. In addition, characterization with atomic force microscopy, variableangle spectroscopic ellipsometry, Fourier transform infrared transmission, and attenuated total reflection spectroscopy is performed. An amount of 6 = 1 vol % pores inside the polyimide film is detected. The pores are oriented perpendicular to the substrate surface and have a conical shape, yielding a slightly reduced pore size at the substrate/film interface.