TY - JOUR
T1 - Structural bonding of ash (Fraxinus excelsior L.)
T2 - Resistance to delamination and performance in shearing tests
AU - Knorz, Markus
AU - Schmidt, Michael
AU - Torno, Stefan
AU - Van De Kuilen, Jan Willem
PY - 2014/5
Y1 - 2014/5
N2 - The utilization of ash (Fraxinus excelsior L.) allows for a significant enhancement of the load-bearing capacity in structural laminated products. However, such applications fundamentally require high-strength and durable bonds between lamellas and in finger joints. Therefore, the aim of the present survey was to evaluate ash bondings in terms of resistance to delamination (EN 302-2) and shear performance (EN 392). Investigations were performed with five adhesives: phenol-resorcinol-formaldehyde (PRF), melamine-urea-formaldehyde (MUF-1, MUF-2), polyurethane (PUR), emulsion polymer isocyanate (EPI) and varying closed assembly times as key bonding parameter. For all tested adhesives and closed assembly times, the shear test showed high wood failure percentages and bond strength values that compare to solid ash. In contrast, for resistance to delamination, significant differences were found between the adhesives as well as between closed assembly times, with improving resistance to delamination for increasing closed assembly times. The best performance was determined for the PRF-adhesive and long closed assembly times. However, standard requirements for resistance to delamination could not be met by any of the adhesives. The resistance to delamination showed no correlation with the shear performance for any of the adhesives. Microscopic examination of the bonded joints revealed that both the penetration behavior of the adhesives and glueline thicknesses clearly correlated with the closed assembly time.
AB - The utilization of ash (Fraxinus excelsior L.) allows for a significant enhancement of the load-bearing capacity in structural laminated products. However, such applications fundamentally require high-strength and durable bonds between lamellas and in finger joints. Therefore, the aim of the present survey was to evaluate ash bondings in terms of resistance to delamination (EN 302-2) and shear performance (EN 392). Investigations were performed with five adhesives: phenol-resorcinol-formaldehyde (PRF), melamine-urea-formaldehyde (MUF-1, MUF-2), polyurethane (PUR), emulsion polymer isocyanate (EPI) and varying closed assembly times as key bonding parameter. For all tested adhesives and closed assembly times, the shear test showed high wood failure percentages and bond strength values that compare to solid ash. In contrast, for resistance to delamination, significant differences were found between the adhesives as well as between closed assembly times, with improving resistance to delamination for increasing closed assembly times. The best performance was determined for the PRF-adhesive and long closed assembly times. However, standard requirements for resistance to delamination could not be met by any of the adhesives. The resistance to delamination showed no correlation with the shear performance for any of the adhesives. Microscopic examination of the bonded joints revealed that both the penetration behavior of the adhesives and glueline thicknesses clearly correlated with the closed assembly time.
UR - http://www.scopus.com/inward/record.url?scp=84899636885&partnerID=8YFLogxK
U2 - 10.1007/s00107-014-0778-8
DO - 10.1007/s00107-014-0778-8
M3 - Article
AN - SCOPUS:84899636885
SN - 0018-3768
VL - 72
SP - 297
EP - 309
JO - European Journal of Wood and Wood Products
JF - European Journal of Wood and Wood Products
IS - 3
ER -