T1 - Selective reinforcement of steel with CF/PA 6 composites in a laser tape placement process
T2 - 17th European Conference on Composite Materials, ECCM 2016
AU - Stokes-Griffin, Chris
AU - Ehard, Stefan
AU - Kollmannsberger, Andreas
AU - Compston, Paul
AU - Drechsler, Klaus
N1 - Publisher Copyright:
© 2016, European Conference on Composite Materials, ECCM. All rights reserved.
PY - 2016
Y1 - 2016
N2 - This paper investigates the possibility of manufacturing hybrid metal/composite laminates in a laser tape placement process. Unidirectionally reinforced carbon fibre/PA 6 composite tapes were applied to 2.0 mm mild steel substrates. The effect of two surface treatments to the steel substrates were investigated 1) grit blast and 2) application of a 60 μm PA 6 film. The effect of laser bias angle was also studied. The interfacial bond strength of the hybrid laminates was determined by means of lap shear tests following the ASTM D 5868 standard. Direct placement onto steel was unsuccessful due to the high laser reflectivity, however placement onto PA 6 coated substrates was successful due to increased laser absorptance. The lap shear strengths as high as 29.5 MPa were achieved for grit blasted and PA 6 coated substrates. The process was found to have a low sensitivity to laser bias angle.
AB - This paper investigates the possibility of manufacturing hybrid metal/composite laminates in a laser tape placement process. Unidirectionally reinforced carbon fibre/PA 6 composite tapes were applied to 2.0 mm mild steel substrates. The effect of two surface treatments to the steel substrates were investigated 1) grit blast and 2) application of a 60 μm PA 6 film. The effect of laser bias angle was also studied. The interfacial bond strength of the hybrid laminates was determined by means of lap shear tests following the ASTM D 5868 standard. Direct placement onto steel was unsuccessful due to the high laser reflectivity, however placement onto PA 6 coated substrates was successful due to increased laser absorptance. The lap shear strengths as high as 29.5 MPa were achieved for grit blasted and PA 6 coated substrates. The process was found to have a low sensitivity to laser bias angle.
KW - Automated Tape Placement (ATP)
KW - Carbon fibre
KW - PA 6
KW - Selective reinforcement
KW - Steel
UR - http://www.scopus.com/inward/record.url?scp=85018616258&partnerID=8YFLogxK
M3 - Conference contribution
AN - SCOPUS:85018616258
T3 - ECCM 2016 - Proceeding of the 17th European Conference on Composite Materials
BT - ECCM 2016 - Proceeding of the 17th European Conference on Composite Materials
PB - European Conference on Composite Materials, ECCM
Y2 - 26 June 2016 through 30 June 2016
ER -