SCHWINGUNGSRISSKORROSION AM STAHL X 20 Cr 13 BEI ZUGSCHWELLBEANSPRUCHUNG IN CHLORIDIONENHALTIGEN MEDIEN BEI TEMPERATUREN BIS ZU 200 degree C.

Karlheinz G. Schmitt-Thomas; Hans M. Tensi; Alfred Leidig; Robert Schmid

SCHWINGUNGSRISSKORROSION AM STAHL X 20 Cr 13 BEI ZUGSCHWELLBEANSPRUCHUNG IN CHLORIDIONENHALTIGEN MEDIEN BEI TEMPERATUREN BIS ZU 200 degree C.

Translated title of the contribution: Fatigue Stress Corrosion Cracking of Steel X20Cr13 Under Pulsating Tensile Stress in Media Containing Chloride Ions at Temperatures up to 200 degree C.

Karlheinz G. Schmitt-Thomas
, Hans M. Tensi
, Alfred Leidig
, Robert Schmid

Research output: Contribution to journal › Article › peer-review

8 Scopus citations

Abstract

The 0. 2% C, 13% Cr steel, in the quenched and tempered condition, was tested under conditions simulating the operating conditions of a steam turbine. The media were 15% MgCl//2, 27% NaCl, and 3% NaCl solutions. Compared with tests in air, corrosion fatigue strengths decreased with increase to the boiling points of the solutions. At temperatures above the boiling points, an increase of corrosion fatigue was observed in NaCl, but not in MgCl//2 solutions. The mechanisms of this behavior are explained by the results of microfractography investigations.

Translated title of the contribution	Fatigue Stress Corrosion Cracking of Steel X20Cr13 Under Pulsating Tensile Stress in Media Containing Chloride Ions at Temperatures up to 200 degree C.
Original language	German
Pages (from-to)	223-227
Number of pages	5
Journal	Arch Eisenhuettenwes
Volume	46
Issue number	3
State	Published - 1975
Externally published	Yes

Cite this

@article{7fd1ca7a6cfa4dea85e556176cb0f2fa,

title = "SCHWINGUNGSRISSKORROSION AM STAHL X 20 Cr 13 BEI ZUGSCHWELLBEANSPRUCHUNG IN CHLORIDIONENHALTIGEN MEDIEN BEI TEMPERATUREN BIS ZU 200 degree C.",

abstract = "The 0. 2\% C, 13\% Cr steel, in the quenched and tempered condition, was tested under conditions simulating the operating conditions of a steam turbine. The media were 15\% MgCl//2, 27\% NaCl, and 3\% NaCl solutions. Compared with tests in air, corrosion fatigue strengths decreased with increase to the boiling points of the solutions. At temperatures above the boiling points, an increase of corrosion fatigue was observed in NaCl, but not in MgCl//2 solutions. The mechanisms of this behavior are explained by the results of microfractography investigations.",

author = "Schmitt-Thomas, \{Karlheinz G.\} and Tensi, \{Hans M.\} and Alfred Leidig and Robert Schmid",

year = "1975",

language = "Deutsch",

volume = "46",

pages = "223--227",

journal = "Arch Eisenhuettenwes",

issn = "0003-8962",

number = "3",

}

TY - JOUR

T1 - SCHWINGUNGSRISSKORROSION AM STAHL X 20 Cr 13 BEI ZUGSCHWELLBEANSPRUCHUNG IN CHLORIDIONENHALTIGEN MEDIEN BEI TEMPERATUREN BIS ZU 200 degree C.

AU - Schmitt-Thomas, Karlheinz G.

AU - Tensi, Hans M.

AU - Leidig, Alfred

AU - Schmid, Robert

PY - 1975

Y1 - 1975

N2 - The 0. 2% C, 13% Cr steel, in the quenched and tempered condition, was tested under conditions simulating the operating conditions of a steam turbine. The media were 15% MgCl//2, 27% NaCl, and 3% NaCl solutions. Compared with tests in air, corrosion fatigue strengths decreased with increase to the boiling points of the solutions. At temperatures above the boiling points, an increase of corrosion fatigue was observed in NaCl, but not in MgCl//2 solutions. The mechanisms of this behavior are explained by the results of microfractography investigations.

AB - The 0. 2% C, 13% Cr steel, in the quenched and tempered condition, was tested under conditions simulating the operating conditions of a steam turbine. The media were 15% MgCl//2, 27% NaCl, and 3% NaCl solutions. Compared with tests in air, corrosion fatigue strengths decreased with increase to the boiling points of the solutions. At temperatures above the boiling points, an increase of corrosion fatigue was observed in NaCl, but not in MgCl//2 solutions. The mechanisms of this behavior are explained by the results of microfractography investigations.

UR - https://www.scopus.com/pages/publications/0016485706

M3 - Artikel

AN - SCOPUS:0016485706

SN - 0003-8962

VL - 46

SP - 223

EP - 227

JO - Arch Eisenhuettenwes

JF - Arch Eisenhuettenwes

IS - 3

ER -

SCHWINGUNGSRISSKORROSION AM STAHL X 20 Cr 13 BEI ZUGSCHWELLBEANSPRUCHUNG IN CHLORIDIONENHALTIGEN MEDIEN BEI TEMPERATUREN BIS ZU 200 degree C.

Abstract

Other files and links

Fingerprint

Cite this