Effect of Thermal Stimulus on Kinetic Rehydration of Thermoresponsive Poly(diethylene glycol monomethyl ether methacrylate)- block-poly(poly(ethylene glycol) methyl ether methacrylate) Thin Films Probed by In Situ Neutron Reflectivity

The kinetic rehydration of thin di-block copolymer poly(diethylene glycol monomethyl ether methacrylate)-block-poly(poly(ethylene glycol) methyl ether methacrylate) (PO₂-b-PO₃₀₀) films containing two thermoresponsive components is probed by in situ neutron reflectivity (NR) with different thermal stimuli in the D₂O vapor atmosphere. The transition temperatures (TTs) of PO₂and PO₃₀₀blocks are 25 and 60 °C, respectively. After the one-step stimulus (rapid decrease in temperature from 60 to 20 °C), the film directly switches from a collapsed to a fully swollen state. The rehydration process is divided into four steps: (a) D₂O condensation, (b) D₂O absorption, (c) D₂O evaporation, and (d) film reswelling. However, the film presents a different rehydration behavior when the thermal stimulus is separated into two smaller steps (first decrease from 60 to 40 °C and then to 20 °C). The film first switches from a collapsed to a semiswollen state caused by the rehydrated PO₃₀₀blocks after the first step of thermal stimulus (60 to 40 °C) and then to a swollen state induced by the rehydrated PO₂blocks after the second step (40 to 20 °C). Thus, the kinetic responses are distinct from that after the one-step thermal stimulus. Both the time and extent of condensation as well as evaporation processes are significantly reduced in these two smaller steps. However, the final states of the rehydrated PO₂-b-PO₃₀₀films are basically identical irrespective of the applied thermal stimulus. Thus, the final state of thermoresponsive di-block copolymer films is not affected by the external thermal stimuli, which is beneficial for the design and preparation of sensors or switches based on thermoresponsive polymer films.