Spray coated indium-tin-oxide-free organic photodiodes with PEDOT:PSS anodes

Morten Schmidt; Aniello Falco; Marius Loch; Paolo Lugli; Giuseppe Scarpa

doi:10.1063/1.4899044

Spray coated indium-tin-oxide-free organic photodiodes with PEDOT:PSS anodes

Morten Schmidt, Aniello Falco, Marius Loch, Paolo Lugli, Giuseppe Scarpa

Default

Technische Universität München

Publikation: Beitrag in Fachzeitschrift › Artikel › Begutachtung

22 Zitate (Scopus)

Abstract

In this paper we report on Indium Tin Oxide (ITO)-free spray coated organic photodiodes with an active layer consisting of a poly(3-hexylthiophen) (P3HT) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) blend and patterned poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) electrodes. External quantum efficiency and current voltage characteristics under illuminated and dark conditions as well as cut-off frequencies for devices with varying active and hole conducting layer thicknesses were measured in order to characterize the fabricated devices. 60% quantum efficiency as well as nearly four orders of magnitude on-off ratios have been achieved. Those values are comparable with standard ITO devices.

Originalsprache	Englisch
Aufsatznummer	107132
Fachzeitschrift	AIP Advances
Jahrgang	4
Ausgabenummer	10
DOIs	https://doi.org/10.1063/1.4899044
Publikationsstatus	Veröffentlicht - 1 Okt. 2014

Zugriff auf Dokument

10.1063/1.4899044

Andere Dateien und Links

Verknüpfung zur Publikation in Scopus

Dieses zitieren

@article{9ae2b5f920634dc3b7be7d26ea103cb4,

title = "Spray coated indium-tin-oxide-free organic photodiodes with PEDOT:PSS anodes",

abstract = "In this paper we report on Indium Tin Oxide (ITO)-free spray coated organic photodiodes with an active layer consisting of a poly(3-hexylthiophen) (P3HT) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) blend and patterned poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) electrodes. External quantum efficiency and current voltage characteristics under illuminated and dark conditions as well as cut-off frequencies for devices with varying active and hole conducting layer thicknesses were measured in order to characterize the fabricated devices. 60% quantum efficiency as well as nearly four orders of magnitude on-off ratios have been achieved. Those values are comparable with standard ITO devices.",

author = "Morten Schmidt and Aniello Falco and Marius Loch and Paolo Lugli and Giuseppe Scarpa",

note = "Publisher Copyright: {\textcopyright} 2014 Author(s).",

year = "2014",

month = oct,

day = "1",

doi = "10.1063/1.4899044",

language = "English",

volume = "4",

journal = "AIP Advances",

issn = "2158-3226",

publisher = "American Institute of Physics",

number = "10",

}

TY - JOUR

T1 - Spray coated indium-tin-oxide-free organic photodiodes with PEDOT:PSS anodes

AU - Schmidt, Morten

AU - Falco, Aniello

AU - Loch, Marius

AU - Lugli, Paolo

AU - Scarpa, Giuseppe

PY - 2014/10/1

Y1 - 2014/10/1

N2 - In this paper we report on Indium Tin Oxide (ITO)-free spray coated organic photodiodes with an active layer consisting of a poly(3-hexylthiophen) (P3HT) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) blend and patterned poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) electrodes. External quantum efficiency and current voltage characteristics under illuminated and dark conditions as well as cut-off frequencies for devices with varying active and hole conducting layer thicknesses were measured in order to characterize the fabricated devices. 60% quantum efficiency as well as nearly four orders of magnitude on-off ratios have been achieved. Those values are comparable with standard ITO devices.

AB - In this paper we report on Indium Tin Oxide (ITO)-free spray coated organic photodiodes with an active layer consisting of a poly(3-hexylthiophen) (P3HT) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) blend and patterned poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) electrodes. External quantum efficiency and current voltage characteristics under illuminated and dark conditions as well as cut-off frequencies for devices with varying active and hole conducting layer thicknesses were measured in order to characterize the fabricated devices. 60% quantum efficiency as well as nearly four orders of magnitude on-off ratios have been achieved. Those values are comparable with standard ITO devices.

UR - http://www.scopus.com/inward/record.url?scp=84907990422&partnerID=8YFLogxK

U2 - 10.1063/1.4899044

DO - 10.1063/1.4899044

M3 - Article

AN - SCOPUS:84907990422

SN - 2158-3226

VL - 4

JO - AIP Advances

JF - AIP Advances

IS - 10

M1 - 107132

ER -

Spray coated indium-tin-oxide-free organic photodiodes with PEDOT:PSS anodes

Abstract

Zugriff auf Dokument

Andere Dateien und Links

Fingerprint

Dieses zitieren