Electrical conductivity of the proton conductor BaZr0.9Y0.1O3-δ obtained by high temperature annealing

S. B.C. Duval, P. Holtappels, U. F. Vogt, E. Pomjakushina, K. Conder, U. Stimming, T. Graule

Publikation: Beitrag in FachzeitschriftArtikelBegutachtung

121 Zitate (Scopus)

Abstract

The influence of a high temperature annealing (∼ 2200 °C) on the microstructure and the electrical properties of BaZr0.9Y0.1O3-δ has been examined. The high temperature annealing was achieved using an optical floating zone furnace. The obtained sample is homogeneous with an average grain size of about 5 μm. No additional phases were found in the XRD pattern and the structure was identified to be cubic. After the high temperature annealing, the grain boundary conductivity is increased by approximately two orders of magnitude, while the bulk conductivity remains the same.

OriginalspracheEnglisch
Seiten (von - bis)1437-1441
Seitenumfang5
FachzeitschriftSolid State Ionics
Jahrgang178
Ausgabenummer25-26
DOIs
PublikationsstatusVeröffentlicht - Okt. 2007

Fingerprint

Untersuchen Sie die Forschungsthemen von „Electrical conductivity of the proton conductor BaZr0.9Y0.1O3-δ obtained by high temperature annealing“. Zusammen bilden sie einen einzigartigen Fingerprint.

Dieses zitieren